<<PVC-HA Product Types and Properties Polyvinyl Chloride Resins / Sekisui PVC-HA Heat Deflection Temperature *1 JIS K7207 Load: 0.45MPa *2 JIS K7191 Load: 1.80MPa   Basic Composition Sekisui PVC-HA or PVC 100PHR Tin stabilizers (Liquid) 1.5PHR Tin stabilizers (polymer) 0.5PHR High-grade fatty acid 0.7PHR Ester wax 2.3PHR MBS 10PHR Test specimen molding conditions PVC-HA and PVC Roll: Temperature 200°C   Milling Time 3min. after wrap Press Temperature 200°C   Milling Time 5min. pre-heat     5min. pressure   Molding pressure 7.5MPa Polyvinyl Chloride Resins / Sekisui Compound Applications •Automobile parts: Weather strips, garnishes, roof moldings, parts in the car. •Building material parts: Bathroom doors and panels, and window frames. •Electrical parts: Trunk air outlet panels, wiring ducts, and switch boxes. •Corrosion resistant factory parts: Pipes, joints, valves, channels, and filler. •Industrial equipment, air conditioner parts: Spiral ducts, pump casings, and gear wheels. •Other: IC cases, thread nozzle holders, and engineering plastic dies. Applications Grade Name Heat Deflection Temperature *1 Specific Gravity Tensile Strength Elongation Ratio Charpy impact Strength Izod Impact 23°C Flexural Strength Flexural Modulus 23°C 0°C -20°C C - MPa % kJ/m2 kJ/m2 kJ/m2 kJ/m2 MPa MPa     JIS K7191 JIS K7112 JIS K7113 JIS K7113 JIS K7111 JIS K7111 JIS K7111 JIS K7110 JIS K7171 JIS K7171 High-Heat Resistance Extrusion Grade EH-152F 80°C   80 1.50 46 100 13 - - 11 69 2,850 EH-153F 80°C High weather resistance 80 1.50 46 100 12 - - 11 68 2,790 EH-250F 85°C   85 1.49 51 80 14 - - 14 74 2,620 EH-350F 90°C   90 1.50 49 70 14 - - 12 75 2,750 EH-351F 90°C High weather resistance 90 1.47 51 120 18 - - 20 74 2,650 EH-355F 90°C   90 1.50 49 70 16 - - 15 73 2,700 EH-452H 95°C   95 1.51 49 50 20 - - 22 71 2,600 EH-455H 95°C   95 1.48 49 50 20 - - 22 69 2,600 EH-459KG 95°C   95 1.52 58 60 27       85 2,500 EH-550K 100°C   100 1.54 51 80 11 - - 10 71 2,610 Normal vinyl chloride 70°C   70 1.47 47 150 20 - - 22 64 2,450 High-Heat Resistance Injection Grade / Extrusion Grade SH-215F   82 1.45 53 90 12 - - 12 78 2,550 SH-415K   93 1.46 53 50 15 - - 15 79 2,500 SH-426KG   90 1.50 53 40 11 - - 11 90 2,650 High Impact Grade G-320T   - 1.34 44 200 118 *2 39   - 66 2,350 G-520T   - 1.30 34 140 128 *2 115 *2 98 *2 - 49 1,960 Wood Foaming Grade F-102T   - 1.50 35 40 4   - - 67 3,800 All values are really measured, not guaranteed. Heat Deflection Temperature *1 measured by 1.80Mpa without Anneal   Charpy Impact Strength *2 not broken   Test specimen molding conditions Roll: Temperature 190°C   Milling Time 3min. after wrapping Press Temperature 190°C   Milling Time 5min. pre-heat     5min. pressure   Molding pressure 7.5MPa